BETONLARDA KUZATILADIGAN KORROZIYA SABABLARINI TAHLIL QILISH

Аннотация

The purpose of writing this article is to give information about corrosion of concrete. While much of the discussion around corrosion in concrete typically centers on the steel reinforcement, concrete itself can experience deterioration and degradation through various chemical and physical processes. These forms of “corrosion” do not involve metal but affect the structural integrity and longevity of concrete over time. This article delves into the various causes that lead to the corrosion of concrete, focusing solely on the material without any steel components. Key words: corrosion of concrete, micro-cracking, degradation, bio effect, damage of acid, cement paste, surface deterioration. Betondagi korroziya ko‘pincha po‘lat armaturaning yomonlashishi bilan bog‘liq bo‘lsada, mustahkam beton konstruktsiyalar ham korroziyaning turli shakllaridan aziyat chekishi mumkin. Bu muammolar, birinchi navbatda, betonning o‘zini yomonlashtiradigan kimyoviy reaktsiyalar va atrof-muhit ta'siridan kelib chiqadi. Kislota hujumi, sulfat ta'siri, muzlash-eritish davrlari va agressiv kimyoviy moddalar ta'siri kabi omillar strukturani zaiflashtirishi, uning chidamliligi va mustahkamligini buzishi mumkin. Quyida ushbu tasirlar haqida ma’lumotlar berilgan. 1. Betonning karbonatlanishi Betonda kimyoviy degradatsiyaning eng keng tarqalgan shakllaridan biri karbonatlanishdir. Bu jarayon atmosferadan karbonat angidrid (CO₂) betonning teshiklariga kirib, 293 30-Sentabr, 2024-Yil kaltsiy gidroksidi (Ca(OH) ) bilan reaksiyaga kirishib, kaltsiy karbonat (CaCO ) hosil qilganda 2 3 sodir bo‘ladi. Dastlab bu reaktsiya zararli ko‘rinmasa ham, betonning strukturaviy yaxlitligiga bir nechta salbiy ta'sir ko‘rsatishi mumkin. Ishqoriylikni yo‘qotish: beton tabiiy ravishda gidroksidi bo‘lib, u kimyoviy hujumning ko‘plab shakllariga qarshi turishga yordam beradi. Karbonatlanish betonning pH qiymatini pasaytiradi va uni yanada degradatsiyaga moyil qiladi. Namlik va ifloslantiruvchi moddalarga nisbatan zaiflikning oshishi: karbonatlanish betonning o‘tkazuvchanligini oshirishi mumkin, bu ko‘proq suv va ifloslantiruvchi moddalarning kirib kelishiga imkon beradi va degradatsiyaning boshqa shakllarini tezlashtiradi. 2. Sulfat hujumi Sulfat hujumi betonda sezilarli korroziyaga olib kelishi mumkin bo‘lgan yana bir kimyoviy jarayondir. Hujumning bu shakli beton tuproqda, yer osti suvlarida yoki sanoat oqava suvlarida bo‘lishi mumkin bo‘lgan sulfatlar ta'sirida sodir bo‘ladi. Sulfatlar sement pastasidagi birikmalar bilan reaksiyaga kirishib, ettringit va gips kabi keng mahsulot hosil bo‘lishiga olib keladi. Kengayish va yorilish: ushbu kengaytiruvchi birikmalarning shakllanishi betonning yorilishiga va kengayishiga olib kelishi mumkin, chunki ichki stresslar materialning kuchidan oshib ketadi. Kuch va chidamlilikni yo‘qotish: sulfat hujumi betonning mexanik xususiyatlarini sezilarli darajada kamaytirishi mumkin, bu esa bosim kuchini yo‘qotishiga, o‘tkazuvchanlikning oshishiga va chidamlilikning pasayishiga olib keladi. 3. Ishqor-silikat reaktsiyasi Ishqor-silikat reaktsiyasi-bu sement tarkibidagi gidroksidlar va agregatlarda topilgan kremniyning ba'zi reaktiv shakllari o‘rtasida sodir bo‘ladigan kimyoviy jarayon. Reaksiya suvni yutganda shishib, beton ichidagi ichki bosimga olib keladigan gel hosil qiladi. Kengayish va yorilish: Ishqor-silikat reaktsiyasi gelining shishishi kuchli kengayishga olib kelishi mumkin, bu esa betonning yorilishi va yomonlashishiga olib keladi. Strukturaviy yaxlitlikning pasayishi: vaqt o‘tishi bilan ISR beton konstruktsiyalarning yuk ko‘tarish qobiliyatini sezilarli darajada kamaytirishi va ularni ishdan chiqishga moyil qilishi mumkin. 4. Kaltsiy gidroksidni yuvish Portlandit deb ham ataladigan kaltsiy gidroksidi sement gidratsiyasi jarayonining mahsulotidir va betonning ishqoriyligini saqlashda hal qiluvchi ro‘l o‘ynaydi. Biroq, vaqt o‘tishi bilan betonga singib ketgan suv kaltsiy gidroksidni eritib yuborishi mumkin. 294 30-Sentabr, 2024-Yil Kuchni yo‘qotish: kaltsiy gidroksidni olib tashlash beton matritsani zaiflashtiradi, uning mexanik kuchini kamaytiradi. G‘ovaklikning oshishi: kaltsiy gidroksidi yuvilganda, u bo‘shliqlarni qoldiradi va betonning g‘ovakliligini oshiradi, bu esa uni degradatsiyaning boshqa shakllariga, shu jumladan muzlash-eritish davrlariga va kimyoviy hujumlarga nisbatan zaifroq qiladi. 5. Muzlatish-erish davrlari Beton g‘ovakli va suvni o‘zlashtira oladi, bu esa uni sovuq iqlim sharoitida muzlash- erishdan paydo bo‘ladigan zo‘riqishlarga chidamliligini kamaytiradi. Beton ichidagi suv muzlaganda, u taxminan 9% ga kengayib, ichki bosim hosil qiladi. Takroriy muzlash davrlari vaqt o‘tishi bilan betonga jiddiy jismoniy zarar etkazishi mumkin. Yorilish va uning kengayishi: suvning muzlashidan kelib chiqadigan ichki bosim yorilish va sirt miqyosiga olib kelishi mumkin. Ushbu zarar, ayniqsa, muzlash nuqtasi atrofida harorat tez- tez o‘zgarib turadigan mintaqalarda juda og‘ir. O‘tkazuvchanlikning oshishi: muzlatish