Electron Transport Mechanisms in Polyethylene Terephthalate Membranes

Аннотация

This paper describes carrier transport mechanisms in a polyethylene terephthalate (PET) films and porous PET-based membranes (PMs) obtained by irradiating of pristine PET film with swift heavy ions and subsequent chemical etching in an alkali (NaOH) solution. The obtained PMs had through nanochannels (pores) with an average diameter of 720—750 nm. We observed that in the temperature range 240—300 K, current—voltage characteristics /(V ) of the initial Cu|PET|Cu structure obeyed the improved Mott—Gurney law, which is based on the Mark—Helfrich model for a space-chargc-limited current (SCLC) mcchanism of electron transport. It was found for the first time that creation of nanochannels in the PMs resulted in significant increase in the electric current density (by about 3 orders of magnitude) while maintaining validity of the SCLC mcchanism.