Development Of A New Brand Of Alloy Instead Of 280x29nl Brand Spreadable Cast Alloy

O CLC - · Brand Spreadable Cast Alloy · Nodir Turakhodjaev · Nosir Saidmakhamadov (Tashkent State Technical University, Tashkent, Uzbekistan) · Fatkhulla Abdullaev (Tashkent State Technical University, Tashkent, Uzbekistan) · Shirinkhon Turakhujaeva (terms of the creative Tashkent State Technical University, Tashkent, Uzbekistan) · Zafar Bobodustov (Turin Polytechnic University In Tashkent, Tashkent, Uzbekistan) · Navoi Machine-Building Plant (Turin Polytechnic University In Tashkent, Tashkent, Uzbekistan) · Navoi Region (Turin Polytechnic University In Tashkent, Tashkent, Uzbekistan) · Ulugbek Rakhmanov (Turin Polytechnic University In Tashkent, Tashkent, Uzbekistan)

The American Journal of Engineering and Technology · 03 · 23-27 · 2021

Аннотация

This article a new brand 280X29NL (sample 1) alloy, which is economically inexpensive and corrosive, was developed without changing the chemical composition of high-chromium 280X29NL cast iron and reducing the mechanical properties of the alloy. KEYWORDS Alloy, chrome, ductile, microstructure, carbide, IST - 0,4 induction furnace, SNOL - 7,2 / 1100 muffle furnace, "SPEKTROLAB-10M" equipment, hardness measuring device TK-2M. The US A Journals Volume 03 Issue 03-2021 36 The American Journal of Engineering and Technology IMPACT FACTOR (ISSN – 2689-0984) 2021: 5. 705 Published: March 25, 2021 | Pages: 36-43 Doi: https://doi.org/10.37547/tajet/Volume03Issue03-06 O CLC - 1121105 677

Доказательный фрагмент

«This article a new brand 280X29NL (sample 1) alloy, which is economically inexpensive and corrosive, was developed without changing the chemical composition of high-chromium 280X29NL cast iron and reducing the mechani…»

Образец извлечения

Демо-превью

This article a new brand 280X29NL (sample 1) alloy, which is economically inexpensive and corrosive, was developed without changing the chemical composition of high-chromium 280X29NL cast iron and reducing the mechani… Полный текст публикации CiteX не хранит — доступ к первоисточнику открывается по DOI согласно лицензии издателя и выбранному плану.

doi.org/10.37547/tajet/Volume03Issue03-06
Цитирований
0
Просмотров
0
Тип
Журнал
Страна
Узбекистан
Ключевые слова
Alloy, chrome, ductile, microstructure, carbide, IST - 0, 4 induction furnace, SNOL - 7, 2 / 1100 muffle, hardness measuring device TK-2M, SNOL - 7,2 / 1100 muffle furnace
Открыть DOI
Спросить CiteX об этой работе

Смежные источники